KAIST Unveils Cause of Performance Degradation in Electric Vehicle High-Nickel Batteries: "Added with Good Intentions
<(From left in the front row) Professor Nam-Soon Choi, Professor Dong-Hwa Seo, (back row, from left) Ph.D candidate Gihoon Lee, Ph.D candidate Seung Hee Han, Ph.D candidate Jae-Seung Kim, (top) M.S candidate Junyoung Kim>
High-nickel batteries, which are high-energy lithium-ion batteries primarily used in electric vehicles, offer high energy density but suffer from rapid performance degradation. A research team from KAIST has, for the first time globally, identified the fundamental cause of the rapid deterioration (degradation) of high-nickel batteries and proposed a new approach to solve it.
KAIST announced on December 3rd that a research team led by Professor Nam-Soon Choi of the Department of Chemical and Biomolecular Engineering, in collaboration with a research team led by Professor Dong-Hwa Seo of the Department of Materials Science and Engineering, has revealed that the electrolyte additive 'succinonitrile (CN4), which has been used to improve battery stability and lifespan, is actually the key culprit causing performance degradation in high-nickel batteries.
In a battery, electricity is generated as lithium ions travel between the cathode and the anode. A small amount of CN4 is included in the electrolyte to facilitate the movement of lithium. The research team confirmed through computer calculations that CN4, which has two nitrile (-CN) structures, attaches excessively strongly to the nickel ions on the surface of the high-nickel cathode.
The nitrile structure is a 'hook-like' structure, where carbon and nitrogen are bound by a triple bond, making it adhere well to metal ions. This strong bonding destroys the protective electrical double layer (EDL) that should form on the cathode surface. During the charging and discharging process, the cathode structure is distorted (Jahn-Teller distortion), and even electrons from the cathode are drawn out to the CN4, leading to rapid damage of the cathode.
Nickel ions that leak out during this process migrate through the electrolyte to the anode surface, where they accumulate. This nickel acts as a 'bad catalyst' that accelerates electrolyte decomposition and wastes lithium, further speeding up battery degradation.
Various analyses confirmed that CN4 transforms the high-nickel cathode surface into an abnormal layer deficient in nickel, and changes the normally stable structure into an abnormal 'rock-salt structure'.
This proves the dual nature of CN4: while useful in LCO batteries (lithium cobalt oxide), it actually causes the structural collapse in high-nickel batteries with a high nickel ratio.
This research holds significant meaning as a precise analysis that goes beyond simple control of charging/discharging conditions, to even elucidating the actual electron transfer occurring between metal ions and electrolyte molecules. Based on this achievement, the research team plans to develop a new electrolyte additive optimized for high-nickel cathodes.
<Schematic diagram of the ligand coordination between CN₄ molecules and Ni³⁺ on the high-nickel cathode surface and the cathode structural degradation process>
Professor Nam-Soon Choi stated, "A precise, molecular-level understanding is essential to enhance battery lifespan and stability. This research will pave the way for the development of new additives that do not excessively bond with nickel, significantly contributing to the commercialization of next-generation high-capacity batteries."
This research, jointly led by Professor Nam-Soon Choi, Seung Hee Han, Junyoung Kim, and Gihoon Lee of the Department of Chemical and Biomolecular Engineering, and Professor Dong-Hwa Seo and Jae-Seung Kim of the Department of Materials Science and Engineering as co-first authors, was published online on November 14th in the prestigious international journal 'ACS Energy Letters' and was selected as the cover article.
※ Paper Title: Unveiling Bidentate Nitrile-Driven Structural Degradation in Ultra-High-Nickel Cathodes,
https://doi.org/10.1021/acsenergylett.5c02845
<Cover Page of International Journal(ACS Energy Letters)>
The research was supported by Samsung SDI.
2025.12.03 View 3467 -
A Study Shows Reactive Electrolyte Additives Improve Lithium Metal Battery Performance
Stable electrode-electrolyte interfaces constructed by fluorine- and nitrogen-donating ionic additives provide an opportunity to improve high-performance lithium metal batteries
A research team showed that electrolyte additives increase the lifetime of lithium metal batteries and remarkably improve the performance of fast charging and discharging. Professor Nam-Soon Choi’s team from the Department of Chemical and Biomolecular Engineering at KAIST hierarchized the solid electrolyte interphase to make a dual-layer structure and showed groundbreaking run times for lithium metal batteries.
The team applied two electrolyte additives that have different reduction and adsorption properties to improve the functionality of the dual-layer solid electrolyte interphase. In addition, the team has confirmed that the structural stability of the nickel-rich cathode was achieved through the formation of a thin protective layer on the cathode. This study was reported in Energy Storage Materials.
Securing high-energy-density lithium metal batteries with a long lifespan and fast charging performance is vital for realizing their ubiquitous use as superior power sources for electric vehicles. Lithium metal batteries comprise a lithium metal anode that delivers 10 times higher capacity than the graphite anodes in lithium-ion batteries. Therefore, lithium metal is an indispensable anode material for realizing high-energy rechargeable batteries. However, undesirable reactions among the electrolytes with lithium metal anodes can reduce the power and this remains an impediment to achieving a longer battery lifespan. Previous studies only focused on the formation of the solid electrolyte interphase on the surface of the lithium metal anode.
The team designed a way to create a dual-layer solid electrolyte interphase to resolve the instability of the lithium metal anode by using electrolyte additives, depending on their electron accepting ability and adsorption tendencies. This hierarchical structure of the solid electrolyte interphase on the lithium metal anode has the potential to be further applied to lithium-alloy anodes, lithium storage structures, and anode-free technology to meet market expectations for electrolyte technology.
The batteries with lithium metal anodes and nickel-rich cathodes represented 80.9% of the initial capacity after 600 cycles and achieved a high Coulombic efficiency of 99.94%. These remarkable results contributed to the development of protective dual-layer solid electrolyte interphase technology for lithium metal anodes.
Professor Choi said that the research suggests a new direction for the development of electrolyte additives to regulate the unstable lithium metal anode-electrolyte interface, the biggest hurdle in research on lithium metal batteries.
She added that anode-free secondary battery technology is expected to be a game changer in the secondary battery market and electrolyte additive technology will contribute to the enhancement of anode-free secondary batteries through the stabilization of lithium metal anodes.
This research was funded by the Technology Development Program to Solve Climate Change of the National Research Foundation in Korea funded by the Ministry of Science, ICT & Future Planning and the Technology Innovation Program funded by the Ministry of Trade, Industry & Energy, and Hyundai Motor Company.
- PublicationSaehun Kim, Sung O Park, Min-Young Lee, Jeong-A Lee, Imanuel Kristanto, Tae Kyung Lee, Daeyeon Hwang, Juyoung Kim, Tae-Ung Wi, Hyun-Wook Lee, Sang Kyu Kwak, and NamSoon Choi, “Stable electrode-electrolyte interfaces constructed by fluorine- and nitrogen-donating ionic additives for high-performance lithium metal batteries,” Energy Storage Materials,45, 1-13 (2022), (doi: https://doi.org/10.1016/j.ensm.2021.10.031)
- ProfileProfessor Nam-Soon ChoiEnergy Materials LaboratoryDepartment of Chemical and Biomolecular EngineeringKAIST
2021.12.16 View 15564